I-S-Glass Fibre amandla aphezulu
I-S-Glass Fibre amandla aphezulu
Imicu yengilazi enamandla amakhulu eyenziwe ngohlelo lwengilazi ye-magnesium alumino silicate ehlangabezana nezidingo zokusetshenziswa kwezempi iye yathuthukiswa futhi yafakwa ekukhiqizweni kwevolumu kusukela ngeminyaka yama-70's & 90's ngokulandelana.
Uma kuqhathaniswa nefayibha ye-E Glass, ikhombisa amandla aqinile angama-30-40% aphezulu, i-16-20% imodulus ephakeme yokunwebeka. ukuphuka, ukuguga okuphezulu & ukumelana nokugqwala, izakhiwo ezikhipha inhlaka esheshayo.
| Isici | |
| ● Amandla amahle okubamba. ● Imoduli ephezulu yokunwebeka ●100 kuya ku-150 degrees celsius ukubekezelela okungcono kwezinga lokushisa ● Ukumelana nokukhathala okuphindwe ka-10 ●Ukumelana nomthelela omuhle kakhulu ngenxa yobude obuphakeme bokuphuka ●Ukuguga okuphezulu nokumelana nokugqwala ●Izindawo zokumanzisa inhlaka esheshayo ●Ukonga isisindo ngokusebenza okufanayo |  |
Isicelo
Izimboni ze-Aerospace, zasolwandle nezezikhali ngenxa yamandla azo aqinile aqinile kanye nemodulus ephakeme yokunwebeka uma iqhathaniswa ne-e-glass.
Ishidi losuku le-S-Glass ne-E-glass
| Ishidi Ledatha le-S-Glass & E-Glass | ||
|
|
| |
| Izakhiwo | I-S-Glass | I-E-Glass |
| I-Virgin Fiber Tensile Strength(Mpa) | 4100 | 3140 |
| I-Tensile Strength(Mpa) ASTM 2343 | 3100-3600 | 1800-2400 |
| I-Tensile Modulus(Gpa) ASTM 2343 | 82-86 | 69-76 |
| I-Elongation To Break(%) | 4.9 | 4.8 |
Izakhiwo
| Izakhiwo | BH-HS2 | I-BH-HS4 | Ingilazi ye-E |
| Amandla e-Virgin fiber tensile (Mpa) | 4100 | 4600 | 3140 |
| Amandla e-Tensi1e(MPA) ASTM2343 | 3100-3600 | 3300-4000 | 1800-2400 |
| I-Tensile Modulus (GPa)ASTM2343 | 82-86 | 83-90 | 69-76 |
| I-elongation to break(%) | 49 | 54 | 48 |