I-Phenolic Fiberglass Molding Tape

incazelo emfushane:

I-4330-2 Phenolic Glass Fiber Molding Compound for Electrical Insulation (High Power Fixed Length Fibers) Ukusetshenziswa: Ifanele ukugqumisa izingxenye zesakhiwo ngaphansi kwezimo zobukhulu obuzinzile namandla okusebenza aphezulu, futhi ifanele ukusetshenziswa ezindaweni ezinomswakama, futhi ingacindezelwa kanye namashubhu esilinda namanxeba.


  • amandla okugoba:≥130-790 MPa
  • amandla omthelela:≥45-239 kJ/m²
  • amandla okubamba:≥80-150 MPa
  • I-Martin imelana nokushisa:≥280℃, ukusebenza okuzinzile ngaphansi kwezinga lokushisa eliphezulu
  • Imininingwane Yomkhiqizo

    Omaka bomkhiqizo

    Ukubunjwa Kwezinto Ezibalulekile Nokulungiselela
    I-Ribbon phenolic glass fiber molding compounds yakhiwa ngokusebenzisa i-phenolic resin njenge-binder, ifaka imicu yengilazi engena-alkali (engase ibe yinde noma igxile ku-chaotically), bese iyomisa futhi ibumbe ukwenza i-ribbon prepreg. Ezinye izilungisi zingase zengezwe ngesikhathi sokulungiselela ukuze kuthuthukiswe ukucutshungulwa noma izici ezithile ze-physicochemical.
    Ukuqinisa: Imicu yengilazi inikeza amandla aphezulu emishini kanye nokumelana nomthelela;
    I-resin matrix: ama-phenolic resins anikeza ukumelana nokugqwala kokushisa kanye nezakhiwo zokufakwa kukagesi;
    Izengezo: zingafaka izinto ezibuyisela amalangabi, okothambisa, njll., kuye ngezidingo zohlelo lokusebenza.
    Izimpawu Zokusebenza

    Izinkomba zokusebenza Ipharamitha ububanzi/izimpawu
    Izakhiwo zemishini Amandla e-Flexural ≥ 130-790 MPa, amandla okuthinta ≥ 45-239 kJ/m², amandla okubamba ≥ 80-150 MPa
    Ukumelana nokushisa Ukushisa kuka-Martin ≥ 280 ℃, izinga lokushisa eliphezulu lokuzinza
    Izakhiwo zikagesi ukumelana nendawo ≥ 1 × 10¹² Ω, ukumelana nevolumu ≥ 1 × 10¹⁰ Ω-m, amandla kagesi ≥ 13-17.8 MV/m
    Ukumuncwa kwamanzi ≤20 mg (ukumuncwa kwamanzi aphansi, alungele izindawo ezinomswakama)
    Ukuncipha ≤0.15% (ukuzinza kwe-dimensional ephezulu)
    Ukuminyana 1.60-1.85 g/cm³ (ilula futhi amandla aphezulu)

    i-phenolic fiberglass composite

    Ukucubungula Ubuchwepheshe

    1. Izimo zokucindezela:

    • Izinga lokushisa: 150±5°C
    • Ingcindezi: 350±50kg/cm²
    • Isikhathi: 1-1.5 imizuzu/mm ukujiya

    2. Indlela yokwenza: i-lamination, i-compression molding, noma i-low-pressure molding, ifanele izimo eziyinkimbinkimbi ze-strip noma izingxenye zesakhiwo ezifana neshidi.

    Izinkambu Zokusebenza

    • Ukufakwa kukagesi: izinto zokulungisa kabusha, izivikeli zezimoto, njll. Zifaneleka kakhulu izindawo ezishisayo nezinomswakama;
    • Izingxenye zemishini: izingxenye zesakhiwo eziqinile (isb. izindlu ezithwalayo, amagiya), izingxenye zenjini yezimoto;
    • I-Aerospace: izingxenye ezingasindi, ezimelana nezinga lokushisa eliphezulu (isb., abakaki bangaphakathi bendiza);
    • Inkundla yokwakha: izisekelo zamapayipi angagqwali, izifanekiso zokwakha, njll.

    Isitoreji Nezinyathelo Zokuqapha

    • Izimo zokubeka: Kufanele ibekwe endaweni epholile neyomile ukuze kugwenywe ukumuncwa komswakama noma ukuwohloka kokushisa; uma kuthintwa umswakama, kufanele kubhakwe ku-90±5℃ imizuzu engu-2-4 ngaphambi kokusetshenziswa;
    • Impilo yeshelufu: ukuze isetshenziswe phakathi nezinyanga ezi-3 kusukela ngosuku lokukhiqiza, ukusebenza kudinga ukuphinda kuhlolwe ngemva kosuku lokuphelelwa yisikhathi;
    • Vimbela ukucindezela okunzima: ukuvimbela ukulimala kwesakhiwo se-fiber.

    Isibonelo semodeli yomkhiqizo

    I-FX-501: Ukuminyana 1.60-1.85 g/cm³, Amandla e-Flexural ≥130 MPa, Amandla kagesi ≥14 MV/m;
    I-4330-1 (isiqondiso esingcolile): izingxenye zesakhiwo ezinamandla aphezulu zokuvikela izindawo ezinomswakama, amandla okugoba ≥60 MPa.

    Izicelo-3